F60 is an epoxy resin-based super high-expansion styrofoam with a starting temperature of 100°C and a maximum temperature of 150°C, which can reach 60 times.

Application Area:

Badminton racket and fishing instead of wind pipe, the amount of each badminton racket is about 2 grams
Carbon fiber is used as a supplementary adhesive for yarn supplement during secondary molding, and is wrapped around the outside of the yarn supplement. It is expanded during secondary hot pressing or baking to provide external pressure.

Features :

Epoxy system,wonderful molecular binding
High operational performance ,Soft materials
Good liquidity when moulding
High strength and high extensibility
High density and Light weight
Fiber construction inside

Specification :

Apperance	Pale yellow
Expansion ratio	1:60 to 100
Thickness(mm)	0.4+/-0.05MM
Volatiles	<0.5%
Initial density(g/cm3)	1.00+/-0.10
Curing process	120℃60min,150℃30min
Tg(℃)	120
Sheft life	-0℃ 6 months
Out life	25℃2months

Epoxy Resin Based Up To 60 Times High Expansion Foam

Carbon Fiber Raw Material

Carbon Fiber Composite Materials

Carbon Fiber Prepreg

Carbon Fiber Fabric

Coated Fiberglass Fabric

Carbon Fiber Ice Hockey Stick

Carbon Fiber Products

Composite Foam Core

Polyacrylonitrile Carbon Fiber

Fiberglass Yarn

Composite Resin Material

Coated Fabric

Carbon Fiber Surfboard

Epoxy Resin Based Up To 60 Times High Expansion Foam

high expansion polyurethane foam

extruded polystyrene foam application

expanded polypropylene foam